6517 si-mn

When steel is added to manganese iron alloy, it can be better reduced, and it can also enhance the toughness, hardness, strength, and elasticity of steel

When steel is added to manganese iron alloy,and it can also enhance the toughness, hardness, strength, and elasticity of steel. Silicon is also an effective graphitizing medium, which can turn the carbon in cast iron into free graphitic carbon. Standard gray cast iron and ductile cast iron need to add at least 4% silicon. Most of the manganese and silicon elements are added to the molten steel in the form of ferromanganese, silicomanganese, and ferrosilicon.

Silicon is also an effective graphitizing medium, which can turn the carbon in cast iron into free graphitic carbon. Standard gray cast iron and ductile cast iron need to add at least 4% silicon.

Silicon is also an effective graphitizing medium, which can turn the carbon in cast iron into free graphitic carbon. Standard gray cast iron and ductile cast iron need to add at least 4% silicon. Most of the manganese and silicon elements are added to the molten steel in the form of ferromanganese,

An alloy of iron, silicon and manganese used in metallurgy, foundry industry, in the production of welding electrodes, etc. The content of manganese from 65 to 75 percent.

Silicon calcium manganese deoxygenation has strong ability to deoxygenate and remove inclusions, low melting point, fast melting speed, good fluidity, and can effectively shorten refining time and reduce refining power consumption.

Standard gray cast iron and ductile cast iron need to add at least 4% silicon. Most of the manganese and silicon elements are added to the molten steel in the form of ferromanganese, silicomanganese, and ferrosilicon.

Manganese can also increases the size of silicon and aluminum deoxidizer deoxidization effect. All that need to be to join a small amount of manganese steel capital as the desulfurizer

Manganese is one of the most main deoxidizer in steelmaking process, almost all types of steel need to DNA by manganese. Because when deoxidization with manganese to generated oxygen product melting point is lower